Development Of Zn-Mn02 Battery Using Chitosan-Znci2.Gel Polymer Electrolytes.
Loading...
Date
2008
Authors
Mohamad, Ahmad Az'min
Journal Title
Journal ISSN
Volume Title
Publisher
Abstract
This project is divided into two main sections, that is to produce solid polymer electrolyte (SPE) as a proton conductor (H+) and to fabricate polymeric solid-state protonic battery with configuration of zinc (Zn)/SPE/manganese (IV) oxide (Mn02)' 1.0 g of chitosan was dissolved in 100 ml of 1 % acetic acid solution.
Projek ini dibahagikan kepada dua bahagian utama iaitu penghasilan elektrolit polimer pepejal (SPE) sebagai
konduktor proton (H+) dan fabrikasi bateri proton keadaan pepejalpolimer dengan konfigurasi zink (Zn)/SPE/mangan dioksida (Mn02)' 1.0 g kitosan dilarutkan dalam 100 mllarutan asid asetik 1 %. Garam ammonium nitrat (NH4N03) dan bahan pemplastik etilena karbonat (EC) ditarnbahkan ke dalam larutan kitosan tersebut.
Description
Keywords
Kitosan , Ammonia Nitrat , Etilina Karbonat , elektrolit polimer , bateri proton , Chitosan , ammonium nitrate , ethylen carbonate , polymer electrolyte , protonic battery