The Uv-Shielding Property Of Zr0.7ce0.3o2-Kaolinite/Exfoliated Kaolinite Composites Prepared By Differentsynthesis Methods

Loading...
Thumbnail Image
Date
2013-05
Authors
Nallis, Kry
Journal Title
Journal ISSN
Volume Title
Publisher
Universiti Sains Malaysia
Abstract
Kaolinite was obtained by elutriation of tin slime, which was then exfoliated by planetary ball milling with 40 wt. % of urea for 1, 3 and 5 hours. Then the kaolinite and urea-treated kaolinite samples were characterized by using XRD, XRF, SEM, FTIR, and BET. The characterization results of kaolinite and urea-treated kaolinite samples for 1, 3 and 5 hours proved that kaolinite was successfully exfoliated by urea treatment for 5 hours and the XRD result of kaolinite showed minor gibbsite and muscovite as impurities. Composites of Zr0.7Ce0.3O2-kaolinite/exfoliated kaolinite were prepared by three different in-situ synthesis methods and one solid mixing method. The first in-situ synthesis method was a citric acid complexing method, with and without NH3 added; the second in-situ synthesis method was a soft solution chemical method; and the third in-situ synthesis method was a hydrothermal treatment method with and without sodium oleate added. For the solid mixing method, Zr0.7Ce0.3O2, which was prepared by the three different synthesis methods such as a citric acid complexing method without NH3 added, a soft solution chemical method and a hydrothermal treatment without sodium oleate added, was solid mixed with kaolinite/exfoliated kaolinite using an agate mortar and pestle.
Description
Keywords
Uv-Shielding Property Of Zr0.7ce0.3o2-Kaolinite , Exfoliated Kaolinite Composites
Citation